Ce Certificated Anticorrosion Wraping Heat Shrink Tape for Protection Steel Pipeline
Usage
Radiation cross-linked Polyethylene (PE) Heat Shrinkable Sleeve is mainly used in anti-corrosion, repairing of oil gas pipeline,is fit for 3PE oil gas steel pipe, 2PE steel pipe, thermal insulating pipe, Epoxy powder coating, and PE drainage pipe etc. We have National Patent certifications.
Oil gas pipe field joint coating
Pre-insulated pipe joint sealing
Drainage pipe joint sealing
Advantage
Radiation crosslinked PE heat shrinkable sleeve is made by basic material and melt adhesive. Our product is with strong adhesion to make sure good quality of project; easier operation, quick shrinking, low cost, perfect anti-water permeating, anti-chemical corrosion, good insulativity and aging resistance, is ideal material of anti-corrosion and thermal insulating system.
EVA is imported. Brand Matsui Japan or Dupont USA
We sold it to Vietnam,Sudan, Kenya, Russia, Kazakhstan,Australia, Turkey etc.
Specifications
---3 Layer PE Coating Pipe
---Offeshore &Underground
---Oil, Gas,Water pipeline
---DIA2''-72''
---Pipeline size: from Ø 108 to Ø 1554 ( 4''---60'')
Sleeves width: 100mm, 150mm,200mm, 300mm,450mm,500mm,600mm,900mm
Closure patch: 100mm, 150mm,200mm (4'', 6'', 8'')
Product Structure
The inner layer is two-components epoxy primer which coated on steel pipe;
Intermediate level is special hot melt adhesive;
Outer layer is modified radiation crossing linking polyethylene backing.
Features & Benefits
Heat Shrinkable Sleeves provide great corrosion protection, Superior resistance to Cathodic Disbondment and excellent durability against abrasion and chemical attack. The result is effective, good performance of sealing, wide application, easy to operate and preheating temperature low (50 °C) ,long term protection against corrosion.
Cross-linked backing provides superior abrasion, mechanical and chemical attack resistance.
High performance adhesive provides excellent resistance to Cathodic Disbondment to ensure long-term corrosion protection.
Just-in-time customized lengths allow bulk rolls to be field cut to protect any pipe size
Open sleeve configuration allows the product to be applied after the pipeline has been welded and cleaned.
Patent certification
| NO |
Text Item |
Unit |
Performance
|
Text Result |
Text Method |
| Back Material |
| 1 |
Tensile Strength |
MPa |
≥17 |
19.47 |
ASTM D638 |
| 2 |
Elongation |
% |
≥400 |
626 |
ASTM D638 |
| 3 |
Vicat Softening Point |
ºC |
≥90 |
92 |
ASTM D1525 |
| 4 |
Brittleness Temperature |
ºC |
<-65 |
<-65 |
ASTM D2671C |
| 5 |
Dielectric Strength |
MV/m |
≥25 |
33.13 |
ASTM D149 |
| 6 |
Volume Resistivity |
Ω.m |
≥1*1013 |
1.1*1013 |
ASTM D257 |
| 7 |
Environment Stress Crack |
h |
≥1000 |
>1000 |
GB/T1842 |
8 |
Chemical
resistance
(7d) |
10%
HCI |
Tensile strength |
MPa |
≥85 |
104.9 |
ASTM D638 |
| Elongation |
% |
≥85 |
96.3 |
ASTM D638 |
10%
NaAH |
Tensile strength |
MPa |
≥85 |
102.1 |
ASTM D638 |
| Elongation |
% |
≥85 |
95.6 |
ASTM D638 |
10%
NaCL |
Tensile strength |
MPa |
≥85 |
108.3 |
ASTM D638 |
| Elongation |
% |
≥85 |
94.1 |
ASTM D638 |
| 9 |
Thermal aging
(150ºC,168h) |
Tensile strength |
MPa |
≥14 |
20.7 |
ASTM D638 |
| Elongation |
% |
≥300 |
630 |
ASTM D638 |
| NO. |
Text Item |
Unit |
Performance
|
Text Result |
Text Method |
| Adhesive |
| 1 |
Softening Point |
ºC |
≥90 |
90.1 |
ASTM E28 |
| 2 |
Brittleness Temperature |
ºC |
<-15 |
<-15 |
ASTM D2671C |
| 3 |
Lap Shear |
MPa |
≥1.0 |
1.5 |
ASTM D1002 |
4 |
Peel Strength
(23±2ºC) |
Steel |
N/cm |
≥70 |
145.6 |
ASTM D1000 |
| Primer |
N/cm |
≥70 |
205.9 |
ASTM D1000 |
| PE layer |
N/cm |
≥70 |
190.0 |
ASTM D1000 |
| Non-solvent Epoxy Primer |
| 5 |
Shear of cured primer |
MPa |
≥5.0 |
12 |
SY/T0041 |